搜索结果: 1-10 共查到“口腔材料学 Filler”相关记录10条 . 查询时间(1.08 秒)
Effect of PMMA filler particles addition on the physical properties of resin composite
PMMA Resin composite Filler
2010/11/30
The aim of this study was to evaluate the effect of additional polymethyl methacrylate (PMMA) fillers on the physical properties of experimental resin composites. PMMA particles (d=30 μm) were added t...
Antibacterial activity of composite resin with glass-ionomer filler particles
Glass-ionomer filler Composite resin Antibacterial activity
2010/11/26
The purpose of this study was to examine the antibacterial activity of composite resin with glass-ionomer filler particles versus that of contemporary commercial composite resins. Three composite resi...
Effect of Thermocycling on Interfacial Gap-formation in Class V Cavities and Mechanical Properties of Spherical Silica Filler Addition to Resin-modified Glass Ionomer Restorations
Resin-modified glass ionomer cement Silanized spherical silica fillers Thermocycled condition
2009/9/15
The effects of thermocycling at 20,000 cycles and addition of silanized spherical silica filler (SF) on resin-modified glass ionomer cement (RMGIC) restorations were investigated. A RMGIC added with a...
Influence of Centrifugal Force on Filler Loading of Resin Composites
Centrifugal force Composite Light-polymerizing apparatus
2009/9/15
This study examined the influence of centrifugal force on the filler loading of composites using a light-polymerizing apparatus combined with a centrifuge. To assess uneven filler particle distributio...
Effect of Spherical Silica Filler Addition on Immediate Interfacial Gap-formation in Class V Cavity and Mechanical Properties of Resin-modified Glass-ionomer Cement
Resin-modified glass-ionomer cement Silanized spherical silica fillers Immediate condition
2009/9/14
The aim of this study was to investigate how the addition of silanized spherical silica filler (SF) would influence the formation of summed, immediate interfacial gaps in Class V tooth cavities. Resin...
Effects of Monomer Composition and Original Filler Content on Filler Loading in the Resulting Centrifuged Composites
Centrifugal force Filler loading Monomer
2009/9/14
This study examined the effects of monomer composition, original filler content, and application of centrifugal force on the resulting filler loading of composites. Either Bis-MPEPP or UDMA was mixed ...
Development of Metal-resin Composite for Dental Magnet Keepers. Part 1: Effects of Filler and 4-META Contents on Setting and Flexural Properties
Resin composite Stainless steel filler Magnet
2009/9/14
Nine kinds of experimental soft magnetic resin composites containing SUS447J1 stainless steel particles as filler were prepared. A UDMA/MAA resin with an MAA mole fraction of 0.67 was used as a matrix...
Effect of Filler Properties in Composite Resins on Light Transmittance Characteristics and Color
Filler Light transmittance Color
2009/9/14
The purpose of this investigation was to examine the effect of filler particle size and shape as well as filler content on light transmittance characteristics and color of experimental composite resin...
Fracture Strength of Direct Surface-retained Fixed Partial Dentures: Effect of Fiber Reinforcement versus the Use of Particulate Filler Composites Only
Fiber-reinforced composite Fracture strength test Particulate filler composite
2009/9/11
This study compared the fracture strengths and analyzed the failure types of direct, surface-retained, anterior fixed-partial-dentures (FPD), reinforced with four types of fiber-reinforced composites ...
Fluoride release and recharge characteristics of denture base resins containing surface pre-reacted glass-ionomer filler
Fluoride releasing and recharging Denture base resin Surface pre-reacted glass-ionomer filler
2009/9/11
The flexural strength, flexural modulus, and the amount of fluoride released from four experimental denture base resins containing 5, 10, 20 and 30 wt% surface pre-reacted glass-ionomer (S-PRG) filler...